Corrosion Behavior of Fe80.22Si8.25Nb10.09Cu1.44 Amorphous Alloy in Alkali Solutions with Additions of Potassium Thiocyanate

V. A. Fedorov; Федоров В. А.; D. V. Balybin; Балыбин Д. В.; T. N. Pluzhnikova; Плужникова Т. Н.; D. Yu. Fedotov; Федотов Д. Ю.; A. D. Berezner; Березнер А. Д.; M. V. Boitsova; Бойцова М. В.

doi:10.31857/S0044185623700237

Corrosion Behavior of Fe80.22Si8.25Nb10.09Cu1.44 Amorphous Alloy in Alkali Solutions with Additions of Potassium Thiocyanate

作者: Fedorov V.A.¹, Balybin D.V.¹, Pluzhnikova T.N.¹, Fedotov D.Y.¹, Berezner A.D.¹, Boitsova M.V.¹
隶属关系:
1. Derzhavin Tambov State University, 392000, Tambov, Russia
期: 卷 59, 编号 2 (2023)
页面: 188-194
栏目: ФИЗИКО-ХИМИЧЕСКИЕ ПРОБЛЕМЫ ЗАЩИТЫ МАТЕРИАЛОВ
URL: https://rjraap.com/0044-1856/article/view/663878
DOI: https://doi.org/10.31857/S0044185623700237
EDN: https://elibrary.ru/SZEMWF
ID: 663878

如何引用文章

全文:

开放存取

##reader.subscriptionAccessGranted##
受限制的访问

订阅存取

详细
作者简介
参考
补充文件
统计

详细

The electrochemical and corrosion behavior of Fe80.22Si8.25Nb10.09Cu1.44 amorphous metal alloy (AMA) was studied in alkali water solutions with the addition of potassium thiocyanate. An increase in the rate of electrode processes (stimulation) in comparison with the base solution was observed at a KSCN concentration of 0.5, 1.0, and 10.0 mM. At a concentration of 5.0 mM, there was a reduction in both cathodic and anodic processes (inhibition). These findings were interpreted within the framework of an electrochemical mechanism and specific structural features of the electrode material. A change in mechanical properties of AMA after exposure of the alkaline medium with a composition of 0.5 М KON + y mM KSCN, where y = 0.5, 1.0, 5.0, and 10.0, was studied. A change in surface roughness has been established. The fracture pattern changed from a brittle cleavage without influence of the environment to the plastic destruction with crack branching and formation of folded structures for all used solutions. After exposure of the 0.5 М KON + 5 mM KSCN solution, a twofold decrease in tensile strength and Young’s modulus was observed. An increase in the KSCN concentration leads to an increase in surface microhardness.

参考

Souza C., Ribeiro D.V., Kiminami C.S. // J. Non-Crystalline Solids. 2016. V. 442. P. 56.
Belkhaoudaa M., Bazzia L., Benlhachemib A., Salghic R., Hammoutid B., Kertite S. // J. Appl. Surf. Sci. 2006. V. 252. P. 7921.
Chattoraj I., Baunack S., Stoica M., Gebert A. // Mater. Corros. 2004. V. 55. P. 36.
Вьюгов П.Н., Дмитренко О.Е. // Вопросы атомной науки и техники. 2004. № 6. С. 185.
Zohdi H., Shahverdi H.R., Hadavi S.M.M. // Electrochem. Commun. 2011. V. 13. P. 840.
Souza C.A.C., May J.E., Oliveira M.F., Kuri S.E., Kiminami C.S., Carlos I.A. // J. Non-Cryst. Solids. 2002. V. 304. P. 210.
Zhai F., Pineda E., Duarte M.J., Crespo D. // J. Alloys Compd. 2014. V. 604. P. 157.
Botta W.J., Berger J.E., Kiminami C.S., Roche V., Nogueir R.P., Bolfarini C. // Journal of Alloys and Compounds. 2014. V. 586. P. S105.
Pang S.J., Zhang T., Asami K., Inoue A. // Mater. Trans. JIM. 2001. V. 42. P. 376.
Gostin P.F., Gebert A., Schultz L. // Corros. Sci. 2010. V. 52. P. 273.
Kuznetsov V.V., Filatova E.A., Telezhkina A.V., Kruglikov S.S. // J. Solid State Electrochemistry. 2018. V. 22. P. 2267.
Liqun M., Inoue A. // Mater. Lett. 1999. V. 38. P. 58.
Inoue A., Takeuchi A. // Intermetallics. 2010. V. 18. P. 1779.
Lu Z.P., Liu C.T., Porter W.D. // Appl. Phys. Lett. 2003. V. 83. P. 2581.
Gostin P.F., Oswald S., Schultz L., Geber A. // Corros. Sci. 2012. V. 62. P. 112.
Guo R.Q., Zhang C., Yang Y., Peng Y., Liu L. // Intermetallic. 2012. V. 30. P. 94.
Lopez M.F., Escudero M.L., Vida E. // Electroquim. Acta. 1997. V. 42. P. 659.
Movahedi B., Enayati M., Wong C. // J. Therm. Spray Technol. 2010. V. 19. P. 1093.
Souza C.A.C., Bolfarini C., Botta F.W.J., Andrade Lma L.R.P., Oliveira M.F., Kiminami C.S. // Mater. Res. 2013. V. 16. P. 1.
Wang S.L., Li H.X., Zhang X.F., Yi S. // Mater. Chem. Phys. 2009. V. 113. P. 878.
Zhang Z.C., CLong Z.L., Peng J., Wei H.Q., Tang P., Li X.G. // Rare Metal Mater. Eng. 2010. V. 39. P. 162.
Кабанов Б.Н., Лейкис Д.И. // Доклады АН СССР. 1947. V. 58. № 8. P. 1685.
Кабанов Б.Н., Бурштейн P.X., Фрумкин А.К. // Dis. Faraday Soс. 1947. V. l. P. 259.
Дамаскин Б.Б., Петрий О.А., Цирлина Г.А. Электрохимия. М.: Химия, КолосС, 2006. С. 496.
Розенфельд И.Л. Ингибиторы коррозии. М.: Химия, 1977. С. 252.
Вигдорович В.И., Цыганкова Л.Е. Кинетика и механизм электродных реакций в процессах коррозии металлов. Тамбов: Издательство Першина Р.В., 2010. С. 50.
Цыганкова Л.Е., Вигдорович В.И. Ингибиторы коррозии металлов. Тамбов: Издательство Першина Р.В., 2010. С. 136.
Рябов А.В., Окишев К.Ю. Новые металлические материалы и способы их производства. Издательство ЮУрГУ, Челябинск, 2007. С. 11.
Гохштейн А.Я. // Электрохимия. 1970. Т. 6. № 7. С. 979.
Хориути Д., Тоя Т. Хемособция водорода. Поверхностные свойства твердых тел / Под. ред. Грина М. М.: Мир, 1972. С. 1.
Тоя Т., Ито Т., Иши Ш. // Электрохимия. 1978. Т. 14. № 5. С. 703.