Structural suppression of blister formation on the tungsten surface under + implantation with an energy of 30 keV

封面

如何引用文章

全文:

开放存取 开放存取
受限制的访问 ##reader.subscriptionAccessGranted##
受限制的访问 订阅或者付费存取

详细

The influence of ultrafine-grained structure and cone-shaped surface morphology on the formation of blisters under irradiation of tungsten with He+ ions with energy of 30 keV has been studied. In comparative experiments, ultrafine-grained and fine-grained samples with an average grain size of 300 nm and 7 μm, respectively, with smooth and cone-shaped surface morphology were used. The ultrafine-grained structure in tungsten samples was obtained by severe plastic deformation, and the cone-shaped surface morphology was obtained by high-fluence irradiation with Ar+ ions with the energy of 30 keV. It was found that blisters are formed on both fine-grained and ultrafine-grained samples when irradiated with He+ ions with a fluence of 1018 ion/cm2. On the fine-grained samples, some of the blisters were with the lids removed, while in the ultrafine-grained samples, all blisters were intact. The thickness of the lids, diameter of the blisters depends on the grain size. The cone-shaped surface morphology on ultrafine-grained tungsten was found to suppress blister formation.

全文:

受限制的访问

作者简介

R. Khisamov

Institute for Metals Superplasticity Problems RAS

编辑信件的主要联系方式.
Email: r.khisamov@mail.ru
俄罗斯联邦, Ufa

N. Andrianova

Lomonosov Moscow State University, Skobeltsyn Institute of Nuclear Physics; Moscow Aviation Institute

Email: r.khisamov@mail.ru
俄罗斯联邦, Moscow; Moscow

A. Borisov

Institute for Metals Superplasticity Problems RAS; Lomonosov Moscow State University, Skobeltsyn Institute of Nuclear Physics; Moscow Aviation Institute

Email: r.khisamov@mail.ru
俄罗斯联邦, Ufa; Moscow; Moscow

M. Ovchinnikov

Institute for Metals Superplasticity Problems RAS; Lomonosov Moscow State University, Skobeltsyn Institute of Nuclear Physics

Email: r.khisamov@mail.ru
俄罗斯联邦, Ufa; Moscow

I. Musabirov

Institute for Metals Superplasticity Problems RAS

Email: r.khisamov@mail.ru
俄罗斯联邦, Ufa

R. Timiryaev

Institute for Metals Superplasticity Problems RAS

Email: r.khisamov@mail.ru
俄罗斯联邦, Ufa

R. Mulyukov

Institute for Metals Superplasticity Problems RAS

Email: r.khisamov@mail.ru
俄罗斯联邦, Ufa

参考

  1. Pitts R.A., Bonnin X., Escourbiac F., Frerichs H., Gunn J.P., Hirai T., Kukushkin A.S., Kaveeva E., Miller M.A., Moulton D., Rozhansky V., Senichenkov I., Sytova E., Schmitz O., Stangeby P.C., De Temmerman G., Veselova I., Wiesen S. // Nucl. Mater. Energy. 2019. V. 20. P. 100696. https://doi.org/10.1016/j.nme.2019.100696
  2. Martynenko Y.V., Nagel M.Y. // Plasma Phys. Rep. 2012. V. 38. P. 996. https://doi.org/10.1134/S1063780X12110074
  3. Kajita S., Kawaguchi S., Ohno N., Yoshida N. // Sci. Rep. 2018. V. 8. P. 56. https://doi.org/10.1038/s41598-017-18476-7
  4. Budaev V.P., Fedorovich S.D., Dedov A.V., Karpov A.V., Martynenko Y.V., Kavyrshin D.I., Gubkin M.K., Lukashevsky M.V., Lazukin A.V., Zakharenkov A.V., Sliva A.P., Marchenkov A.Y., Budaeva M.V., Tran Q.V., Rogozin K.A., Konkov A.A., Vasilyev G.B., Burmistrov D.A., Belousov S.V. // Plasma Discharge. Fusion Science and Technology. 2023. V. 79. Iss. 4. P. 404. https://doi.org/10.1080/15361055.2022.2118471
  5. Harutyunyan Z.R., Ogorodnikova O.V., Aksenova A.S., Gasparyan Y.M., Efimov V.S., Kharkov M.M., Kaziev A.V., Volkov N.V. // J. Surf. Invest.: X-Ray, Synchrotron Neutron Tech. 2020. V. 14. № 6. P. 1248. https://doi.org/10.1134/S1027451020060245
  6. Mulyukov R.R. // J. Vac. Sci. Technol. B. 2006. V. 24. P. 1061. https://doi.org/10.1116/1.2174024
  7. Wu Y-C., Hou Q-Q., Luo L-M., Zan X., Zhu X-Y., Li P., Xu Q., Cheng J-G., Luo G-N., Chen J-L. // J. Alloys Compd. 2019. V. 779. P. 926. https://doi.org/10.1016/j.jallcom.2018.11.279
  8. Efe M., El-Atwani O., Guo Y, Klenosky D.R. // Scr. Mater. 2014. V. 70. P. 31. https://doi.org/10.1016/j.scriptamat.2013.08.013
  9. El-Atwani O., Hattar K., Hinks J.A., Greaves G., Harilal S.S., Hassanein A. // J. Nucl. Mater. 2015. V. 458. P. 216. http://doi.org/10.1016/j.jnucmat.2014.12.095
  10. Chen Z., Niu L-L., Wang Z., Tian L., Kecskes L, Zhu K., Wei Q. // Acta Mater. 2018. V. 147. P. 100. https://doi.org/10.1016/j.actamat.2018.01.015
  11. Wurmshuber M., Doppermann S., Wurster S., Jakob S., Balooch M., Alfreider M., Schmuck K., Bodlos R., Romaner L., Hosemann P., Clemens H., Maier-Kiener V., Kiener D. // Int. J. Refract. Met. Hard Mater. 2023. V. 111. 106125. https://doi.org/10.1016/j.ijrmhm.2023.106125
  12. Qian W., Wei R., Zhang M., Chen P., Wang L., Liu X., Chen J., Ni W., Zheng P. // Mater. Lett. A. 2022. V. 308. P. 130921. https://doi.org/10.1016/j.matlet.2021.130921
  13. Cuomo J.J., Ziegler J.F., Woodall J.M. // Appl. Phys. Lett. 1975. V. 26. P. 557.
  14. Auciello O. // J. Vacuum Sci. Technol. 1981. V. 19. P. 841. http://doi.org/10.1116/1.571224
  15. Qin W., Ren F., Doerner R.P., Wei G., Lv Y., Chang S., Tang M., Deng H., Jiang C., Wang Y. // Acta Mater. 2018. V. 153. P. 147. https://doi.org/10.1016/j.actamat.2018.04.048
  16. Zhang Y., Ganeev A.V., Wang J.T., Liu J.Q., Alexandrov I.V. // Mater. Sci. Eng. A. 2009. V. 503. P. 37. https://doi.org/10.1016/j.msea.2008.07.074
  17. Yusupova N.R., Krylova K.A., Mulyukov R.R. // Lett. Mater. 2023. V. 13. Iss. 3. P. 255. https://doi.org/10.22226/2410-3535-2023-3-255-259
  18. Mulyukov R.R., Khisamov R.K., Borisov A.M., Baimiev A.Kh., Ovchinnikov M.A., Timiryaev R.R., Vladimirova A.A. // Lett. Mater. 2023. V. 13. Iss. 4s. P. 444. https://doi.org/10.22226/2410-3535-2023-4-373-376
  19. Danilenko V.N., Parkhimovich N.Y., Kiekkuzhina L.U., Gunderov D.V. // Lett. Mater. 2023. V. 13. Iss. 4. P. 373. https://doi.org/10.22226/2410-3535-2023-4-444-449
  20. Li P., Sun D-Z., Wang X., Xue K.-M., Hua R., Wu Y.-C. // Trans. Nonferrous Metals Society of China. 2018. V. 28. Iss. 3. P. 461. https://doi.org/10.1016/S1003-6326(18)64679-5
  21. Xue K., Guo Y., Zhou Y., Xu B., Li P. // Int. J. Refr. Met. Hard Mater. 2021. V. 94. P. 105377. https://doi.org/10.1016/j.ijrmhm.2020.105377
  22. Khisamov R.K., Andrianova A.A., Borisov A.M., Ovchinnikov M.A., Timiryaev R.R., Musabirov I.I., Mulyukov R.R. // Phys. Atomic Nuclei. 2023. V. 86. № 10. P. 2198. https://doi.org/10.1134/S1063778823100228
  23. Mashkova E.S., Molchanov V.A. Medium-Energy Ion Reflection from Solids. Amsterdam: North-Holland, 1985. 444 p.
  24. Khisamov R.K., Andrianova A.A., Borisov A.M., Ovchinnikov M.A., Musabirov I.I., Timiryaev R.R., Mulyukov R.R. // Phys. Atomic Nuclei. 2024. V. 87. № 9. P. 1. https://doi.org/10.1134/S1063778824090151
  25. Andrianova N.N., Borisov A.M., Ovchinnikov M.A., Khisamov R.K, Mulyukov R.R. // Bull. Russ. Acad. Sci. Phys. 2024. V. 88. P. 478. https://doi.org/10.1134/S1062873823706141
  26. Xiao S., Ma Y., Tian L., Li M., Qi C., Wang B. // Nucl. Mater. Energy. 2020. V. 23. P. 100746. https://doi.org/10.1016/j.nme.2020.100746
  27. Zhang M., Zhao J., Meng X., Chen Z., Wang Q., Guan X. Wang T. // J. Nucl. Sci. Tech. 2021. V. 58: Iss. 10. P. 1071. https://doi.org/10.1080/00223131.2021.1911872
  28. Guseva M.I., Martynenko Y.V. // Sov. Phys. Usp. 1981. V. 24. P. 996. https://doi.org/10.1070/PU1981v024n12ABEH004758
  29. Behrisch R., Eckstein W. Sputtering by Particle Bombardment. Berlin, Heidelberg: Springer-Verlag, 2007. 509 p. https://doi.org/10.1007/978-3-540-44502-9
  30. Fan C., Pan S., Hu X., He B., Huang M. // Acta Materialia. 2023. V. 254. P. 118993. https://doi.org/10.1016/j.actamat.2023.118993
  31. EerNisse E.P., Picraux S.T. // J. Appl. Phys. 1977. V. 48. P. 9. https://doi.org/10.1063/1.323332
  32. Wei Q., Zhang H.T., Schuster B.E., Ramesh K.T., Valiev R.Z., Kecskes L.J., Dowding R.J., Magness L., Cho K. // Acta Materialia. 2006. V. 54. P. 4079. https://doi.org/10.1016/j.actamat.2006.05.005
  33. Xu A., Wei T., Short K., Palmer T., Ionescu M., Bhattacharyya D., Smith G.D.W., Armstrong D.E. J. // J. Mater Sci. 2023. V. 58. P. 10501. https://doi.org/10.1007/s10853-023-08647-5
  34. Allen F.I., Hosemann P., Balooch M. // Scripta Mater. 2020. V. 178. P. 256. https://doi.org/10.1016/j.scriptamat.2019.11.039
  35. Guseva М.I., Ivanov S.М., Martynenko Y.V. // J. Nucl. Mater. 1981. V. 96. P. 208. https://doi.org/10.1016/0022-3115(81)90235-X

补充文件

附件文件
动作
1. JATS XML
下载
2. Fig. 1. SEM images obtained in the backscattered electron detection mode of the morphology of the initial (ingot) (a); ultrafine-grained (b); fine-grained (c) tungsten samples.

下载 (61KB)
索引源数据
3. Fig. 2. SEM images obtained in the secondary electron detection mode of the surface of fine-grained (a) and ultrafine-grained (b, c) tungsten samples after irradiation with He+ ions.

下载 (58KB)
索引源数据
4. Fig. 3. SEM images obtained in the secondary electron detection mode of the surface layer of fine-grained (a) and ultrafine-grained (b) tungsten samples irradiated with He+ ions.

下载 (26KB)
索引源数据
5. Fig. 4. SEM images obtained in the secondary electron detection mode at an angle of 45°: fine-grained (a) and ultrafine-grained (b) tungsten samples after irradiation with Ar+ ions.

下载 (72KB)
索引源数据
6. Fig. 5. SEM images obtained at an angle of 45°: fine-grained (a, b) and ultrafine-grained (c, d) tungsten samples after preliminary irradiation with Ar+ and subsequent irradiation with He+.

下载 (107KB)
索引源数据

版权所有 © Russian Academy of Sciences, 2025