Combustion in the 2Co–Ti–Al system was observed by high-speed video recording. It is established that combustion occurs in the frontal mode, and the process parameters are determined. The maximum rate of the combustion temperature increase from the moment of initiation to the maximum value reached 2.7 · 104 K/s. The front propagation velocity calculated from the video recording was 9.4 cm/s. A micro-hotspot mode of combustion of the reaction composition was found. The temperature dependences of the electrical resistivity and magnetic moment of the single-phase Co2TiAl product synthesized in the combustion mode have been measured. For the synthesized Co2TiAl sample, the Curie temperature is Tc = 120 ± 5 K, and the electrical resistivity at room temperature is 1.35 μOhm · m. It is shown that the electrical and magnetic properties of the Co2TiAl alloy obtained in the combustion mode are similar to those of alloys obtained by arc melting.

全文:

受限制的访问

作者简介

M. Busurina

Merzhanov Institute of Structural Macrokinetics and Materials Science, Russian academy of sciences

编辑信件的主要联系方式.
Email: busurina@ism.ac.ru
俄罗斯联邦, Chernogolovka

A. Sytschev

Merzhanov Institute of Structural Macrokinetics and Materials Science, Russian academy of sciences

Email: busurina@ism.ac.ru
俄罗斯联邦, Chernogolovka

S. Vadchenko

Merzhanov Institute of Structural Macrokinetics and Materials Science, Russian academy of sciences

Email: busurina@ism.ac.ru
俄罗斯联邦, Chernogolovka

A. Karpov

Merzhanov Institute of Structural Macrokinetics and Materials Science, Russian academy of sciences

Email: busurina@ism.ac.ru
俄罗斯联邦, Chernogolovka

参考

  1. F. Appel, H. Clemens, F. Fischer, J. Progress Mater. Sci. 81, P. 55 (2016). https://doi.org/10.1016/j.pmatsci.2016.01.001
  2. S.K. Dolukhanyan, A.G. Aleksanyan, G.N. Muradyan et al, Russ. J. Phys. Chem. B 15, 740 (2021). https://doi.org/10.1134/S1990793121040035
  3. R. De Groot, F. Mueller, P. Engen et al., Phys. Rev. Lett. 50, 2024 (1983). https://doi.org/10.1103/PhysRevLett.50.2024
  4. A.N. Vasilyev, V.D. Buchel’nikov, T. Takagi et al., Physics-Uspekhi. 46, 559 (2003). https://doi.org/10.1070/pu2003v046n06abeh001339
  5. Т. Graf, G. Fecher, J. Barth et al., J. Phys. D: Appl. Phys. 42, 084003 (2009). https://doi.org/10.1088/0022-3727/42/8/084003
  6. Yu.A Perevozchikova, N.I. Kourov, S.M. Emel’yanova et al, Mezhdunarodnyj zhurnal prikladnyh i fundamental’nyh issledovanij. 3, 539 (2016). https://appliedresearch.ru/ru/article/view?id=8928&ysclid=ll6qs1l7xz185782893
  7. B. Fadila, M. Ameri, D. Bensaid et al., J. of Magnetism and Magnetic Materials. 448, 208 (2018). https://doi.org/10.1016/j.jmmm.2017.06.048
  8. M. Koller, T.Chráska, J. Cinert et al., Materials and Design. 126, 351 (2017). https://doi.org/10.1016/j.matdes.2017.04.028
  9. W. Zhang, L. Zhao, Z. Qian et al., J. Alloys Compounds. 431, 65 (2007). https://doi.org/10.1016/j.jallcom.2006.05.083
  10. V.I. Itin, Yu.S. Naiborodenko High-temperature synthesis of intermetallic compounds, Tomsk, Ed. by Tomsk University, 1989 [in Russian].
  11. M. L. Busurina, A.E. Sytschev, A.V. Karpov et al., Russ. J. Phys. Chem. B 14, 999 (2020). https://doi.org/10.1134/S1990793120060020
  12. S.L. Silyakov, M.Yu. Shiryaeva, A.F. Belikova et al., Russ. J. Phys. Chem. B 16, 290 (2022). https://doi.org/10.1134/S1990793122020129
  13. J. Liang, L. Zhu, L.V. Wang, Light Sci. Appl. 7, 42 (2018) https://doi.org/10.1038/s41377-018-0044-7
  14. A.S. Mukasyan, S. Hwang, A.E. Sytchev et al., Combust. Sci.Techn. 115, 335 (1996). https://doi.org/10.1080/00102209608935535
  15. A.S. Rogachev, A.S. Mukasyan, Combust. Explos. Shock Waves. 51, 53 (2015).
  16. N.A. Kochetov, B.S. Seplyarskii, Russ. J. Phys. Chem. B 17, 381 (2023). https://doi.org/10.1134/S1990793123020082
  17. A.S. Rogachev, S.G.Vadchenko, N.V. Sachkova et al., Dokl. Phys. Chem. 478, 27 (2018). https://doi.org/10.1134/S0012501618020021
  18. M.L.Busurina, A.E. Sychev, I.D. Kovalev et al., Combust. Explos. Shock Waves. 56(3), 317 (2020). https://doi.org/10.1134/S0010508220030089
  19. S. Mizusaki, T. Ohnishi, T.C. Ozawa et al., Transactions on Magnetics. 47, 2444 (2011). https://doi.org/10.1109/TMAG.2011.2159581
  20. A.S. Shcherbakov, A.F. Prekul, R.V. Pomorcev, Pis’ma v ZHETF. 32(6), 425 (1980) [in Russian].

补充文件

附件文件
动作
1. JATS XML
下载
2. Fig. 1. Video frames of the SHS process of a sample of the 2Co + Ti + Al composition in a vacuum, obtained using a high-speed video camera.

下载 (23KB)
索引源数据
3. Fig. 2. Thermogram of the SHS process of the reaction mixture of the composition 2Co+Ti+Al in a vacuum.

下载 (11KB)
索引源数据
4. Fig. 3. Micro-foci on the surface of the combustion front of the 2Co+Ti+Al composition.

下载 (7KB)
索引源数据
5. Fig. 4. Photo of the sample before (1) and after synthesis (2).

下载 (13KB)
索引源数据
6. Fig. 5. Photograph of the microstructure of the surface of a section of a sample of combustion products of a 2Co−Ti−Al mixture and the results of EDA (wt.%).

下载 (20KB)
索引源数据
7. Fig. 6. Temperature dependence of the magnetic moment M of the synthesized Co2TiAl sample cooled in zero magnetic field and a magnetic field H = 10 kA/m.

下载 (16KB)
索引源数据
8. Fig. 7. a – Temperature dependence of specific electrical resistance; b – dependence of ln{σ(T)−σ0} on T−1/4 for the synthesized Co2TiAl sample.

下载 (21KB)
索引源数据

版权所有 © Russian Academy of Sciences, 2024